Good quality refractory Converter Self-flow Patching Material

1.Content:MgO80%min C10%min 2.High temperature liquidity 247min(1000degrees) 3.MOQ:20MT 4.As customer's special demands

Converter Self-flow Patching Material

  

Advantage 

1. Well spread, even coverage on the surface of molten iron and steel

2. The content is steady, it has good fluxing capacity, while using won’t cause crust or erode the ladle wall, so it is easy to clean the ladle.

3. Appropriate alkalinity, it won’t pollute the molten iron and steel, meanwhile it can absorb other inclusion

Certificate

1.ISO approval.

2.Certified as "qualified & reliable" manufacturer by CIQ.

3.Mill's test reported as each 1MT/ p.p bag by CIQ. 

Production lead time &shippment

1.Prompt producing after order,with 35 tons capability a day.

2.Shipment with 5 working days after production.(ship to Korea&Japan about 2 days,ship to Brazil(North America) about 35 days)

Specification

Item	Composition(%)		Gravity Density(g/cm3)		Rupture Strengh(MPa)		Porosity(%)		High Temperature Liquidity (mm)
	MgO	C	1000°C	1500°Cx3h	1000°C	1500°Cx3h	1000°C	1500°Cx3h	1000°C
Coverter Self-flow Patching	≥ 80.0	≥ 10.0	≥ 2.4	≥ 2.3	≥12.0	≥ 7.8	≤ 15.0	≤ 15.5	≥247

Good quality refractory Converter Self-flow Patching Material